Method for manufacturing a cellulose product by a pressure moulding apparatus, pressure moulding apparatus and cellulose product

ABSTRACT

The present invention relates to a method of manufacturing a cellulose product having a flat or non-flat product shape by a pressure moulding apparatus comprising a forming mould. The forming mould has a forming surface defining said product shape, The method comprises the steps of: 
     arranging a cellulose blank containing less than 45 weight percent water in said forming mould; heating said cellulose blank to a forming temperature in the range of 100° C. to 200° C.; and pressing said cellulose blank by means of said forming mould with a forming pressure acting on the cellulose blank across said forming surface, said forming pressure being in the range of 1 MPa to 100 MPa.

TECHNICAL FIELD

The present disclosure relates to a method of manufacturing a cellulose product from wood pulp, an apparatus for manufacturing such a cellulose product and a cellulose product.

BACKGROUND

There are many situations where it is desirable to provide two-dimensional (2D) or three-dimensional (3D) shaped objects made of sustainable materials. One such situation relates to packaging of sensitive goods, such as mechanical high precision items, electronic equipment and other household and hardware items, that need protective packaging in order to avoid damage of the sensitive goods, due to for example mechanical shock, vibrations or compression during transport, storage, or other handling. Such packages typically require a protective insert that has a shape adapted to the goods contained, and thus securely holds the goods in the package. Such inserts are commonly made of expanded polystyrene (EPS), which is a lightweight petroleum derived material and is not regarded as a sustainable material.

A low price material commonly used for packaging inserts is moulded pulp. Moulded pulp has the advantage of being considered as a sustainable packaging material, since it is produced from biomaterials and can be recycled after use. As a consequence moulded pulp has been quickly increasing in popularity for both primary and secondary packaging applications (packaging next to the article and assembly of such packages). Moulded pulp articles are generally formed by immersing a suction mould into a pulp suspension, while suction is applied, whereby a body of pulp is formed with the shape of the desired article by fibre deposition. The suction mould is then withdrawn from the suspension and the suction is generally continued to compact the deposited fibres while exhausting residual liquid.

A common disadvantage with all wet-forming techniques is the need for drying of the moulded product, which is a time and energy consuming step. Another drawback is that strong inter-fibre bonds, often explained as hydrogen bonds, are formed between the fibres in the material, which restrict the flexibility of the material.

Moreover, many modern lean production lines require in-line on-demand package or component manufacturing where a wet-forming process not is preferred.

Lately, new fibre-based materials have been developed with the purpose of enabling dry forming of three-dimensional objects. One approach is disclosed by WO2014142714A1. WO2014142714A1 discloses a dry-laid composite web being an intermediate product for thermoforming of three-dimensionally shaped objects, comprising 40-95 wt-% CTMP fibres, 5-50 wt-% thermoplastic material, and 0-10 wt-% additives, wherein the dry-laid composite web has been impregnated with a dispersion, an emulsion, or a solution containing the thermoplastic material, polymer, and dried, obtaining a density of 50-250 kg/m3, or, if compressed by calendaring 400-1000 kg/m3. According to WO2014142714A1, bonding of the polymer is activated by the higher temperature applied in the thermoforming process and contributes to the final strength of the thermoformed object.

Although the polymer according to WO2014142714A1 may be contributing to the final strength and enabling forming of dry-laid web, such thermoplastic ingredient will erase the sustainable features of the cellulose since the composite will not be recyclable. This disadvantage is applicable even if a renewable and compostable bio-plastic, e.g. polylactide (PLA) is used as proposed by WO2014142714A1, since logistics for material recycling is not available.

Recent findings and political decisions, e.g. Paris agreement on global warming 2015, stipulates that the carbon footprint of consumed goods and packages, in so called life cycle analysis (LCA), is highly influenced by the ability to recycle and reuse materials. Even renewable materials like cellulose and PLA must be recycled in order to measure up with multi recycled non-renewable materials like polyethylene terephthalate (PET).

Material recycling is slowly and gradually becoming more and more established in most parts of the world. Europe has the global lead with approximately 30% recycling while United States only has reached 10% and still many development countries has not yet started to recycle. Common for all recycling efforts is a focus on the most frequently used materials such as paper, card board, glass, aluminium, steel and PET. These recyclable fractions represent a vast majority of wasted goods and it is not likely that other fractions, like bio-polymers, will be established as public available recycle logistics in a foreseeable future.

The global demand for 3D formed packages, boxes, cups, plates, bowls, inserts and covers in renewable and recyclable material with mechanical properties close to plastics, is therefore huge.

ISBN 978-91-7501-518-7 (Helena Halonen, October, 2012) has studied one approach—hydroxyethylcellulose (HEC) for creating a new all-cellulose composite material by compression moulding of commercial chemical wood pulps processed with only water. The objective was to study the structural changes during processing and the complexity of relating the mechanical properties of the final bio composites to the nano scale structure.

The combination of high temperature (150-170° C.) and high pressure (45 MPa) during compression moulding yields a remarkable increase in fibril aggregation, possibly including cellulose-cellulose fusion bonds, i.e., fibril aggregation in the fibre-fibre bond region. This fibril aggregation is resulting in a bio-composite with remarkable mechanical properties including improved strength (289 MPa), modulus (12.5 GPa) and toughness (6%) to be compared to e.g. PET-strength (75 MPa) and PET-modulus (PET 3 GPa).

Although WO2014142714A1 proposes non-recyclable thermoplastic ingredient and ISBN 978-91-7501-518-7 presents scientific results for forming recyclable cellulose fibres, to obtain good mechanical properties, no practical or industrial method has so far been invented enabling commercial production, with reasonable cycle time, of packages and gods in cellulose as replacement for plastics which are possible to recycle as cardboard.

SUMMARY

An object of the present disclosure is to provide a method for manufacturing a cellulose product, a cellulose forming apparatus and a cellulose product where the previously mentioned problems are avoided. This object is at least partly achieved by the features of the independent claims. The dependent claims contain further developments of the method for manufacturing a cellulose product, the cellulose forming apparatus and the cellulose product.

There are many situations where it is desirable to provide objects made of sustainable materials in flat or essentially non-flat shapes. A flat shape may refer to a generally two-dimensional shape, such as for example the shape of a sheet material or blank, and essentially non-flat shapes may refer to any suitable three-dimensional object shape. One such situation relates to the packaging of liquids, dry materials and different types of goods, where the packaging may be made in a three-dimensional shape or formed into a three-dimensional shape from a two-dimensional sheet material.

The invention relates to a method of manufacturing a cellulose product having a flat or non-flat product shape by a pressure moulding apparatus comprising a forming mould, the forming mould having a forming surface defining said product shape, comprising the steps of:

-   -   arranging a cellulose blank containing less than 45 weight         percent water in said forming mould;     -   heating said cellulose blank to a forming temperature in the         range of 100° C. to 200° C.; and     -   pressing, said cellulose blank by means of said forming mould         with a forming pressure acting on the cellulose blank across         said forming surface, said forming pressure being in the range         of 1 MPa to 100 MPa.

The forming pressure may be an isostatic pressure or a non-isostatic pressure.

According to a further aspect of the present invention, it is provided a method of manufacturing a cellulose product having a non-flat product shape, comprising the steps of: providing an isostatic pressure moulding apparatus comprising a forming mould having a forming surface defining said product shape, and a pressure mould; arranging a cellulose blank containing less than 45 weight percent water between the forming mould and the pressure mould; heating the cellulose blank to a forming temperature in the range of 100° C. to 200° C.; and pressing, by means of the pressure mould, the cellulose blank against the forming mould with a substantially equal forming pressure acting on the cellulose blank across the forming surface, the forming pressure being in the range of 1 MPa to 100 MPa.

The heating step and the pressing step may at least partly take place at the same time, or the cellulose blank may be pre-heated and no additional heat supplied during pressing.

The cellulose product may for example be a container or a part of a container where the cellulose product manufacturing using the method according to embodiments of the present invention may, for example, replace plastic products that are more difficult to recycle. Accordingly, cellulose products manufactured using the inventive method may, for example, be packages, inserts for packages, boxes, bowls, plates, cups, trays, or covers.

By the term “isostatic” should be understood the volumetric pressure on the fibres, of the heated bio-composite during the process of fibril aggregation, is substantially equal in all geometrical locations of the final 3D object during production.

By the term “non-isostatic” should be understood the volumetric pressure on the fibres, of the heated bio-composite during the process of fibril aggregation, is not equal in all geometrical locations of the final 3D object during production.

The cellulose blank may be provided in various forms, for example as a web, a rug, felt, loose fibres, foam, sheets, etc. The blank might contain minor substances (0-10%) of agents for increasing strength, decreasing hygroscopy or making the final component hydrophobic, flameproof, colouring the component or in other way alter the features of the final material. The amount of additives should however not jeopardize the purpose of this invention to make the components recyclable as cardboard.

The blank may be produced in a pulp converting plant as rug in rolls.

The present invention is based upon the realization that a flat or non-flat cellulose product can be made more homogeneous and with shorter cycle times using an isostatic pressure moulding apparatus. In particular, the present inventors have found that, depending on the desired shape of the cellulose product, an isostatic pressure acting on the cellulose blank may provide for a remarkable decrease in the holding time needed to obtain the same mechanical properties of the final product. The present inventors have also found that, depending on the desired shape of the cellulose product, a non-isostatic pressure acting on the cellulose blank may provide a suitable forming of the cellulose product obtaining desirable mechanical properties of the final product.

In this context it should be noted that the required process time to obtain acceptable mechanical properties of the final product is related to the humidity of the blank and a specific temperature and a specific isostatic or non-isostatic pressure.

A temperature, preferable between 150-170° C., and a pressure, preferable between 3-7 MPa, can generate different mechanical properties. For example, an isostatic temperature of 168° C. and an isostatic pressure of 4.8 MPa at an air humidity of 50% relative humidity will generate a hard and stiff component at a holding time of 10 seconds. Lower temperature and pressure gives softer and more flexible components.

Also too much water in the blank will increase holding times a lot. ISBN 978-91-7501-518-7 describes holding times of 20 minutes and uses essentially wet pulp for the research. Experiments have shown that the optimum water content in the cellulose blank at the time of processing should be in the range 0.5-10% weight.

In severe cases, with large pressure variations, in the blank during bonding, parts of the component will never be acceptable regardless any holding time.

Prior art describes pulp compressing devices using traditional presses with hydraulic cylinders that converts hydraulic pressure, called the pressure media, to a force on a tool or a mould via a piston of the cylinder. When forming non-planar objects, like hollow 3D-objects, a forming mould with positive and negative mould parts, with a cavity representing the desired thickness and shape of the component in between, called mould cavity, which said mould is compressed by the force from the piston. Such a shape defined compressing device will lead to large variations in local pressure in the blank during heat processing, if no compensation to the component thickness versus processing pressure is performed. Any shape defined compressing device, without compensation for obtaining isostatic pressure, may thereby lead to uneven component quality and, in most industrial cases, unacceptable cycle times for production.

Moreover, the inventors have found that the required pressure level drastically can be reduced if an isostatic pressure method is used. ISBN 978-91-7501-518-7 has used a hollow hemisphere as reference object for the research using 45 MPa and 20 minutes in a shape defined compressing device. The internal pressure of the blank in the mould cavity is extremely high on top (by the pole) and close to zero at the bottom (adjacent to the equator). The present inventors have now surprisingly found that, by using an isostatic pressure such an object can be produced with one tenth of the used pressure at holding times counted in seconds.

According to various embodiments of the present invention, the cellulose blank may contain wood pulp. Although so-called mechanical pulp can be used for the cellulose blank, it has been found that chemical wood pulp yields better material properties of the product.

In embodiments, the cellulose blank may comprise at least 90 weight percent wood pulp and thus be almost exclusively made by easily recyclable material.

According to various embodiments, the pressure mould may advantageously comprise a flexible membrane, and the pressure moulding apparatus further comprises a fluid control device for controlling a fluid to exert an isostatic pressure on the cellulose blank via the fluid impermeable membrane.

In this context it should be noted that the term fluid encompasses both liquids and gases.

In some embodiments, the moulding apparatus may contain the pressure fluid in an enclosure partly bounded by the membrane. By increasing the amount of fluid in the enclosure and/or reducing the size of the enclosure, the fluid pressure will increase. The increasing fluid pressure will in turn result in an increased isostatic pressure acting on the cellulose blank.

Accordingly, the above-mentioned fluid control device may be an actuator compressing the fluid or a fluid flow control device for controllable allowing pressurized fluid to enter a pressure chamber having the flexible membrane as a portion of a wall thereof.

In some embodiments, the above-mentioned membrane may be an integral part of the apparatus, and may be used during a large number of pressing operations.

In other embodiments, the membrane may be fixed to the cellulose blank, for instance by means of an adhesive, during pressing, and the method may further comprise the step of providing a new membrane following the pressing step. In these embodiments, the membrane may for example be provided on a roll, and may be added to the manufactured product to add functionality to the product.

In yet further embodiments, the above-mentioned membrane may be provided on the cellulose blank.

According to a further aspect of the present invention, it is provided an isostatic pressure moulding apparatus for manufacturing a cellulose product having a flat or non-flat product shape starting from a cellulose blank, the isostatic pressure moulding apparatus comprising a forming mould having a forming surface defining the product shape; and a fluid control device for controlling a fluid to exert an isostatic pressure on the cellulose blank to press the cellulose blank against the forming surface.

The forming mould may comprise a negative forming mould part and a negative pressure mould part.

The forming mould may comprise a negative forming mould part and a positive pressure mould part.

The invention also relates to a cellulose product manufactured by the described method. The cellulose product is having a flat or essentially non-flat shape.

According to embodiments of the present invention, an isostatic pressure is obtained in force defined compressing devices, wherein said compressing devices comprises a flexible barrier or a membrane surrounding and separating the blank from the pressure media, e.g. gas, hydraulic oil, water, beverages to be packed, elastomer or dilatant material.

A method and a device according to embodiments of the present invention relates to blow moulding of hollow 3D objects like bottles, milk packages, cans and jars. Classic cellulose based packages for dairies and juice experience competition from blow moulded PET-bottles. Despite the fact that cellulose and paper based packages are renewable and recyclable, the mouldabillity of blow moulded PET has restrained the growth for folded paper packages.

According to said blow moulding embodiments, devices comprising, at least two negative forming moulds surrounding said cellulose fibres and a single use film layer barrier, to become an integrated part of the final component, wherein said cellulose fibres and said film layer barrier are provided to the cavity of the moulds in a tube shape and wherein said film layer barrier will separate the pressure media, when filled into said tube shape, from the cellulose fibres and wherein said pressure media will be pressurised to create an isostatic pressure on every portion of said cellulose fibres towards said forming moulds.

The present invention will thereby provide a method, tube shaped blank, a blow moulding device and renewable packages with similar properties as thermoplastics wherein said packages are recyclable as paper and cardboard.

Such a blow moulding device can preferably constitute the filling equipment on site at a diary, brewery or juice factory by using the beverage or liquid to be packed, as said pressure media.

According to other embodiments, an isostatic pressure is obtained in shape defined compressing devices, comprising two rigid moulds, one positive and one negative wherein the cavity between the closed moulds define the shape of the final three dimensional object and wherein the thickness of said cavity or the thickness of said blank, is designed to create an isostatic pressure on every portion of said cellulose fibres towards said moulds.

BRIEF DESCRIPTION OF DRAWINGS

These and other aspects of the present invention will now be described in more detail, with reference to the appended drawings showing example embodiments of the invention, wherein:

FIG. 1a-c schematically show a conventional press method, compressing device and component;

FIG. 2a-b schematically show an alternative configuration of the compressing device, using multi-use membrane, shown initial stage (a) and compressed stage (b) according to an example embodiment of the present invention;

FIG. 3a-b schematically show an alternative configuration of the compressing device, comprising single-use material integrated barrier, shown initial stage (a) and compressed stage (b) according to an example embodiment of the present invention;

FIG. 4a-d schematically show an alternative configuration of the compressing device and component, using single-use material integrated barrier and blow moulding, shown initial stage (a & b) and compressed stage (c) according to an example embodiment of the present invention;

FIG. 5a-b schematically show an alternative configuration of the compressing device, using multi-use membrane, shown initial stage (a) and compressed stage (b) according to an example embodiment of the present invention;

FIG. 6a-c schematically show an alternative configuration of the compressing, using cavity compensating pressure control, shown initial stage (a & b) and compressed stage (c) according to an example embodiment of the present invention;

FIG. 7a-b schematically show an alternative configuration of the compressing device, using blank thickness compensation, shown initial stage (a) and compressed stage (b) according to an example embodiment of the present invention;

FIG. 8a-c schematically show an alternative configuration of the compressing device, using a massive flexible membrane; and

FIG. 9a-c schematically show another alternative configuration of the compressing device, using a massive flexible membrane.

DESCRIPTION OF EXAMPLE EMBODIMENTS

Various aspects of the disclosure will hereinafter be described in conjunction with the appended drawings to illustrate and not to limit the disclosure, wherein like designations denote like elements, and variations of the described aspects are not restricted to the specifically shown embodiments, but are applicable on other variations of the disclosure.

In the present detailed description, a method for manufacturing a cellulose product, a pressure moulding apparatus, and a cellulose product will be described.

Various embodiments of sheet materials or blanks according to the disclosure are mainly discussed with reference to a cellulose blank placed in position for forming in a forming mould, in a flat shape. It should be noted that this by no means limits the scope of the present invention, which equally well includes, for example, a blank pre-shaped into a three-dimensional object. For instance, the blank may be presented to the forming mould in a shape similar to the desired final shape of the object. Another embodiment could comprise a cellulose blank, which is supplied to the mould in a web on a roll.

A flat shape may refer to a generally two-dimensional (2D) shape, such as for example the shape of a blank or a sheet material, and essentially non-flat shapes may refer to any suitable three-dimensional (3D) shape. An object according to the disclosure may be made in a two-dimensional shape, a three-dimensional shape, or formed into a three-dimensional shape from a two-dimensional blank or sheet material.

Moreover, by schematically showing a coherent sheet of cellulose fibres, this will by no means limit the scope of present invention, which equally well includes, for example, blanks with loose and separated fibres applied to the forming mould.

In the present detailed description, various embodiments of the three-dimensional object to be formed and the mould to form the objects according to the present invention are mainly discussed with reference to a hollow bowl, a hollow cup or a hollow bottle, with mainly uniform thickness. It should be noted that this by no means limits the scope of the present invention, which equally well includes, for example, complex shapes with different thickness, non-hollow portions or massive objects. For instance, the object can advantageously comprise stiffeners, creases, holes, 3D shaped text, hinges, locks, threads, snaps, feet, handles or surface patterns.

FIGS. 1a-c illustrate a conventional press method, compressing device and a component produced with non-isostatic pressure method and device.

FIG. 1a is a schematic side view of a prior art compressing device in a non-compressed state having a negative upper mould 102 b and a positive lower forming mould 102 a and a sheet of cellulose fibres 101 a.

FIG. 1b is a schematic side view of a prior art compressing device in a compressed state having a negative upper pressure mould 102 b and a positive lower forming mould 102 a and a sheet of cellulose fibres 101 a partly compressed by the force F forming the desired final shape 101 b by using heat and pressure P.

As is customary, the thickness of the final component 101 b is uniform and consequently the thickness of the cavity t₁=r_(b)−r_(a) between the two moulds 102 a and 102 b is uniform. Since conventional tools for compressing is made of stiff metal, or similar non-flexible material, and since dry cellulose fibres not behave as a pressure equalising fluid, the pressure P in said cavity will depend on the amount of present blank 101 and the local pressure generating principle.

The local pressure generating principle at pressure P₂ and P₅ is defined by the force F. The local pressure generating principle at P₄ is defined by the geometry of the cavity and the amount of present blank 101. The local pressure P₃ is determined by a combination of force and shape defined pressure generating principle.

A shape defined pressure, like P₄, is highly dependent of the actual present amount of blank 101. Small and normally stochastic variations in the local material supply will drastically affect the obtained local pressure. Force defined pressure has linear gain and is a far more robust process for industrial usage.

FIG. 1c illustrate a three dimensional object, component, a hemi sphere 101 b produced with above described conventional compression method. Since it is likely that some blank 101 a will be stretched when the blank 101 a bends over the lower mould 102 a when the upper pressure mould 102 b closes the tool over the blank 101 a, the mechanical properties is different in location 101 b P₄ than in location 101 b P₂ of the finished component 101 b.

A force defined compressing device according to an example embodiment of the present disclosure will now be described with reference to FIGS. 2a-b . In FIG. 2a , a schematic side view of a compressing device or pressure moulding apparatus, in the form of a forming mould 3 for cellulose fibres using heat is shown in an open state. The compressing device or forming mould may be constructed so that an isostatic pressure is applied when forming the cellulose product. The pressure applied may also be non-isostatic so that different pressure levels are applied in different parts of the forming mould 3 when forming the cellulose product. The forming mould 3 comprises at least one forming surface defining said product shape.

The forming mould 3 of this embodiment of the present disclosure uses one stiff forming mould part 2 a placed under a multi-use membrane 4. The membrane 4 constitutes a seal for a pressure media or fluid 5, such as for example hydraulic oil, contained in a pressure chamber, not shown in the figure. The membrane 4, also called diaphragm, can preferably be made of rubber, silicon, elastomer or polyurethane.

Similar press devices are found in completely different industries like for example when forming metal sheets for aircrafts or processing of metallic powder into homogeneous materials. For instance, isostatic presses for conventional purposes normally uses very high pressure, such as within the range 1000-2000 bar.

The cellulose blank 1 a, mainly comprising cellulose fibres with some additives and agents, has as shown in FIG. 2a been placed in a gap between the membrane 4 and the stiff forming mould part 2 a, which in FIG. 2a is arranged below the membrane 4. The cellulose blank 1 a may also contain an amount of water, which for example may depend on the humidity of the surrounding atmosphere.

In order to form the cellulose product, or a part of a cellulose product, from the cellulose blank 1 a, the cellulose blank 1 a, has to be heated to a forming temperature T₁, which may be in the range 100° C. to 200° C. The forming mould part 2 a may be heated to a desired temperature T₂ so that heat is transferred to the cellulose blank 1 a in order to achieve the forming temperature T₁ of the cellulose blank 1 a. The forming mould 3 may for example be pre-heated to a temperature of 150-170° C. by pumping heated oil into internal channels 7 of the forming mould part 2 a. An alternative way to pre-heat the forming mould 3 is to use integrated electrical resistors, not shown in the figure. The cellulose blank 1 a can also be pre-heated, for example by using infrared rays prior to tool entrance. Heating the pressure media 5 to a pressure media temperature T₅ may also be a suitable alternative.

In FIG. 2b , the hydraulic oil 5 has been pressurized to a pressure of at least 1 MPa, and the membrane 4 has wrapped the heated forming mould 2 a with the compressed material 1 b forming the cellulose product in-between. A suitable pressure P₁ when forming the cellulose product may be within the range 1-100 MPa. By applying a suitable pressure P₁, the cellulose fibres are compressed. The applied pressure P₁ may be uniform or isostatic in order to compress the cellulose fibres evenly regardless of their relative position on the forming mould 2 a and regardless of the actual local amount of fibres. In an alternative embodiment, the pressure may instead be non-isostatic so that different pressure levels in different parts of the forming mould 3 are used to form the cellulose product. This may for example be used if different structural properties in different parts of the cellulose product are desired.

The compressing device may comprise a fluid control device (not shown in the figures) and may be an actuator compressing the fluid 5 or a fluid flow control device for controllable allowing pressurized fluid 5 to enter the pressure chamber having the flexible membrane 4 as a portion of a wall thereof. The apparatus may comprise the fluid 5, or the fluid 5 may be air taken from the surrounding atmosphere.

The present inventors has found that a pressure P₁ of 4 MPa (40 bar) at a temperature of 160° C. when forming the cellulose product gives a fibril aggregation in the cellulose fibres that compares with many thermoplastics after 10 seconds of holding time.

In order to reduce the cycle time for industrial production of cellulose products from compressed material 1 b, the cooling of said compressed material 1 b may for example be done by pumping cooled oil into internal channels 7 arranged in the forming mould part 2 a or into the pressure chamber wherein the forming mould part 2 a temperature T₂ and pressure media 5 temperature T₅ quickly can be lowered after the fibril aggregation has completed in the cellulose fibres.

The process and the device will return to its open state shown in FIG. 2a by lowering the pressure media 5 to atmospheric pressure P₀ wherein said membrane 4 will retract to its more or less flat initial state and wherein the finished cellulose product can be ejected and preferable be cut free from unwanted residual compressed or un-compressed cellulose fibres.

The final thickness t₁ of the cellulose product may vary slightly depending on the actual local amount of cellulose fibres.

In an alternative embodiment, a stiff forming mould part may be used instead of the flexible or pliable membrane 4, which may be suitable if different pressure levels are desired when forming the cellulose product. The use of a flexible membrane 4 may provide an isostatic compressing method resulting in a homogeneous cellulose product with high strength and short production cycle time.

One difference between the inventive compressing method and device in FIG. 2a-b when using isostatic pressure and the prior art method and device in FIG. 1 a-b lies in the configuration using a flexible or pliable membrane 4 instead of the stiff upper mould 102 b. An isostatic compressing method and device results in a homogeneous component with high strength and short production cycle time.

Above, one example embodiment of the isostatic compressing method and device was described with reference to FIGS. 2a-b . It should be understood that forming of three-dimensional objects in all-cellulose composite using heated compression moulding of wood pulp processed with only water can be obtained in other ways while still achieving isostatic pressure.

Referring to FIGS. 3a-b , the multi-use membrane 4 in FIGS. 2a-b has been replaced with a single-use membrane comprising a thin film barrier 6 wherein said barrier 6 may be pre-applied to the cellulose blank 1 a when the cellulose blank 1 a was produced or wherein the film barrier 6 is provided to the compressing device, for example from rolls, not shown in the figures, and applied to the cellulose blank 1 a during the isostatic compression of the cellulose blank 1 a.

Said thin film barrier 6 may be made of a thermoplastic material like PET or PLA, having a thickness within the range 1-700 μm.

FIG. 3a schematically shows the method comprising a compressing device or forming mould 3 in its initial open state, using the thin film barrier 6 applied to the cellulose fibres 1 a, comprising a lower negative forming mould part 2 b preheated to temperature T₂ and a pressure media or fluid 5, preferably gas or air at atmospheric pressure, contained in the pressure chamber, not shown in the figure.

FIG. 3b show the same device and cellulose blank 1 a as shown in FIG. 3a in the compressed state wherein said pressure media 5, preferably compressed air or a non-contaminating liquid as water, has been pressurized to the pressure P₁ and wherein the thin film barrier 6 separates and seals the pressure media from the compressed material 1 b of the cellulose blank 1 a and wherein said pressure media 5 and membrane 6 forming equal pressure acting on the cellulose fibres across the heated forming surface, with a temperature T₂, of said forming mould part 2 b.

By holding the equal pressure P₁ at the temperature T₁ for a certain period of time X, the fibril aggregation in the cellulose fibres will create a bio-composite component of the compressed material 1 b with mechanical properties close to thermoplastics. If as an example, the pressure P₁ being 4 MPa (40 bar), the forming temperature T₁ being 140° C., the temperature T₂ of the forming mould part 2 b being 160° C., and the time period X being 10 seconds, the bio-composite component of the compressed material 1 b with mechanical properties close to thermoplastics can be achieved.

By removing the pressure media 5 and lower the pressure to atmosphere pressure P₀ after the time period X the cellulose product formed by the compressed material 1 b can be ejected and if needed cut to its final shape.

One advantage with the method discussed in FIGS. 3a-b is that the film barrier 6 also can function as a barrier towards other media to be exposed to the component during usage. For example, if the cellulose product provided with the film barrier 6 is a bowl for on-the-go salads it is desired to have a barrier 6 to protect the cellulose fibres in the compressed material 1 b from contact with the vegetables and to decrease the hygroscopic features of the bowl. This method could also be used for producing bottles or containers for liquid goods, and the cellulose product may thus be suitable for packaging different types of liquids or beverages, including carbonated liquids.

Turning to FIGS. 4a-d , the forming mould 3 comprises at least two openable and closable negative forming surfaces or parts 2 a, 2 b, surrounding a tube shaped cellulose blank 1 a comprising a film barrier 6 wherein the outer layer is uncompressed cellulose 1 a fibres and its additives and the inner layer 6 a single-use membrane comprising a thin film barrier 6. The blank can preferably be supplied to the compressing device in rolls, not shown in the figure, in flat shape wherein the blank is formed into a tube shape, not shown in the figure, surrounding a pressure media nozzle 8.

In FIG. 4a , the forming mould 3 with the forming surfaces or parts 2 a, 2 b are pre-heated to the forming mould temperature T₂, and are schematically shown in the open initial stage of the forming process method. The tube shaped cellulose blank 1 a with the film barrier 6 is supplied from the top surrounding the fixed pressure media nozzle 8, which means that the tube shaped cellulose blank 1 a with the film barrier 6 is supplied in a direction from above into the forming surfaces 2 a, 2 b.

By closing the pre-heated forming mould 3 with a closing force F_(c) which is higher than an opening force created by the pressure P₁ applied by the pressure media to the inside of the forming mould 3 by the pressure media nozzle 8 shown in FIG. 4c . The closed state of the forming mould 3 with the forming surfaces 2 a, 2 b is schematically shown in FIGS. 4 b-c. The closing force F_(c) and the design of the forming surfaces 2 a, 2 b adjacent to the top and bottom of the cavity will seal the inner volume of the cellulose blank 1 a from the outside atmospheric pressure P₀. In an alternative embodiment, the cellulose blank may be cut by the forming moulds from residual material when the forming mould 3 is closed.

FIG. 4c shows the forming and febrile aggregation phase of the method of present invention wherein said inner volume of the blank has been filled with pressure media 9 from the pressure media nozzle 8 and pressurized to the pressure P₁ wherein the pressure media 9 and the single-use membrane 6 forming equal pressure acting on the cellulose fibres across the heated forming surface of said forming moulds 2 a and 2 b.

The filling process is taking place between the steps shown in FIGS. 4b and 4c , and requires air channels 10 to enable the air outside the cellulose blank 1 a with the film barrier 6 in the cavity of the forming mould 3 to be drained during the blank expansion process.

FIG. 4d illustrates a three dimensional cellulose product in the form of a hollow object made from the compressed material 1 b and the film barrier 6, e.g. a bottle for beverages, formed by the method described in FIG. 4a-c filled with said pressure media 9 wherein the film barrier 6 separates the pressure media 9 from the compressed cellulose fibres 1 b.

According to present disclosure the pressure media 9 is constituted by the beverage that is intended to be filled into the cellulose product, such as e.g. milk, juice, water and carbonated beverages.

The film barrier 6 can preferable be made of a thin thermoplastic material like PET or PLA, having a thickness in the range of 1-700 μm, wherein the film barrier 6, conventionally applied in paper packages for beverages, also seal the cellulose fibres 1 b from contact with the beverage 9 during storage and usage of the cellulose product.

The cycle time for the process step shown in FIG. 4c can be reduced if the beverage 9 is cooled to a temperature T₉, for example in the range of 1-20° C., and filled fast, preferably in less than a second. If the forming mould 3 with the forming surfaces 2 a, 2 b is pre-heated to a mould temperature T₂, which for example is 200° C. and the blank is pre-heated to a temperature T₁, of for example 140° C., the pressure media temperature T₉ will enable release of the filled bottle from the forming mould 3 in cycle times of seconds or even less.

FIG. 5a-b schematically show another principle of the present disclosure, wherein the compressing device comprises at least one positive forming mould part 2 a, at least one negative pressure mould part 2 b and a multi-use pre-shaped membrane 4, wherein the pressure media 5 is pressurized to the pressure P₁ after the mould parts 2 a and 2 b, surrounding the cellulose blank 1 a, has been closed.

The final forming stage where fibril aggregation in the cellulose fibres of the cellulose blank 1 a takes place is shown in FIG. 5b . The enlarged cross section shown in FIG. 5b illustrates how the pressure media 5 penetrates into the forming mould 3 between the upper negative pressure mould part 2 b and the membrane 4 wherein a pressure P₁, uniformly will compress the cellulose blank 1 a towards the forming surface of the pre-heated lower positive forming mould 2 a. The penetration of pressure media 5 can be facilitated by minor indentations, not shown in the figure, in the surface of the upper negative pressure mould part 2 b acting as micro channels for the pressure media 5.

The embodiment of the compressing device according to FIGS. 5a-b may be beneficial compared to the method discussed in FIGS. 2a-b , where shorter cycle times are preferred. The membrane 4 does not have to deform to the same extent in the embodiment shown in FIGS. 5a -b.

The above described examples of the compressing method, with reference to FIGS. 2-5, comprises a flexible membrane 4, which may be used to provide an isostatic pressure. It should be understood that forming of three-dimensional objects in all-cellulose composite using heated compression moulding of wood pulps processed with only water can be obtained using conventional tools while still achieving isostatic pressure.

Referring to FIGS. 6a-c , an upper pre-heated negative non-flexible pressure mould part 2 b and a lower pre-heated positive non-flexible forming mould part 2 a, surrounds the cellulose blank 1 a wherein the cavity thickness t(P) between the lower pre-heated positive non-flexible forming mould part 2 a and the upper pre-heated negative non-flexible pressure mould part 2 b deviates from nominal even thickness where the deviation is theoretically and/or practically established to create an isostatic pressure P₁ on every portion of cellulose blank 1 a towards the mould parts 2 a and 2 b when the mould parts are pressed together with the force F.

FIG. 6a schematically shows the embodiment in an initial open state with the cellulose blank in a flat state fed to the mould parts in a continuous web 1 a. FIG. 6c schematically shows the embodiment in a closed state with the cellulose blank 1 a in a compressed non-flat state. FIG. 6b schematically shows the embodiment in a state in-between the open and the closed, in a non-compressed non-flat state.

FIGS. 6a-c show an example of a compressing device for a hollow bowl, where the positive forming mould part 2 a has a nominal, preferred, shape and where the negative pressure mould part 2 b has a compensated shape in order to obtain equal pressure P₁.

As shown in FIG. 6b the blank is deformed by the two mould parts 2 a, 2 b wherein the thickness t of the cellulose blank 1 a varies due to friction and deformation restrain in the cellulose blank 1 a. In this schematic example, which can be altered in many ways, the cellulose blank 1 a will end up with a thinnest thickness t_(min), adjacent to the cavity entrance of the pressure mould 2 b and a thickest thickness t_(max) on the top of the forming mould 2 a.

The cavity thickness, s, between the two mould parts 2 a, 2 b is therefore compensated so the most narrow cavity thickness s_(min) is situated adjacent to where the cellulose blank is thinnest t_(min) and the most wide cavity thickness s_(max) is situated adjacent to where the un-compressed cellulose blank 1 a is thickest t_(max), by means of the negative pressure mould 2 b, pressing the cellulose blank 1 a against the forming positive mould 2 a with a substantially equal forming pressure P₁ acting on the cellulose blank 1 a across the forming surface.

Moreover, the relation between thickness of the cellulose blank, t, and the cavity thickness, s, and the final cavity shape, is also related to the geometrical pressure generation of the cavity. The force F determines the pressure P₁ on top of the positive forming mould part 2 a while the convexity, thickness and angel of the cavity adjacent to the most narrow cavity thickness s_(min) determines the final pressure P₁.

The inventors of present invention have found that the final shape of the cavity is a complex algorithm t(P) in order to obtain substantially isostatic pressure P₁ where both mathematical, preferably FEM-analysis, and empirical tests, preferably trial-and-error, is required to obtain equal pressure all over the component.

According to another embodiment of the present disclosure, without flexible membrane, the geometrically pressure compensated cavity in FIGS. 6a-c can be substituted with thickness compensation of the cellulose blank.

FIGS. 7a-b schematically show a traditional non-compensated pressure negative forming mould part 2 b and a non-compensated positive forming mould part 2 a, with a preferred equal and nominal cavity thickness, t, wherein the blank has a pressure compensated thickness between t_(min)−t_(max) established with same theory and in the same manner as described for the embodiment discussed in relation to FIGS. 6a -c.

The preference for the method of creating isostatic pressure without flexible membrane, presented in relation to FIGS. 6a-c and 7a-b , relates to shorter cycle time and lower cost for the compressing device. However, the development effort might be more costly for the method using stiff moulds.

The advantage for using the method described in relation to FIGS. 7a-b over the method described in relation to FIGS. 6a-c is the achieved even thickness t₁ of the final cellulose product. However, the blanks might be more costly to produce in the method described in FIGS. 7 a-b.

As an alternative, the forming mould 3 may also be arranged with a membrane constructed as a massive flexible membrane structure. In FIGS. 8a-c an alternative forming mould 3 with a negative forming mould part 2 b and a positive forming mould part 2 a is schematically shown. The positive forming mould part 2 a is applying a forming pressure, F, on a massive flexible membrane 4, which is applying an isostatic pressure on the cellulose blank 1 a when forming the cellulose product. With massive flexible membrane is meant a flexible structure, which has a similar ability to apply the isostatic pressure to the cellulose blank 1 a, as the membrane structures described in the embodiments above, but with a greater elastic deformation zone compared to thinner membrane structures. The massive flexible membrane 4 may be constructed with a thick membrane structure or even be made of a homogeneous body of a flexible material. The flexible material may have properties that will make the material float out between the forming mould parts when pressure is applied to the body. In the embodiment shown in FIGS. 8a-c , the massive flexible membrane 4 is constructed from a homogeneous body of a flexible material.

In an alternative embodiment, the massive flexible membrane 4 may have a varied thickness, where the massive flexible membrane is for example shaped or casted into a structure with a varied thickness. The thinner and thicker areas of the massive flexible membrane with varied thickness may compensate for areas in the forming mould parts which need smaller or bigger deformation of the membrane in order to equalize or even out the pressure subjected to the cellulose blank 1 a. By using a massive flexible membrane structure the forming mould can be made cheaper and simpler in construction.

The massive flexible membrane 4 is constructed so that when the pressure, F, is applied from the forming mould parts, the massive flexible membrane 4 deforms in order to provide the isostatic pressure. The massive flexible membrane 4 may be made of a suitable elastomeric material, such as for example rubber, silicone, polyurethane or other elastomer. Due to the flexible properties of the massive flexible membrane 4, the massive flexible membrane 4 applies an isostatic pressure to the cellulose blank 1 a.

In FIG. 8a , the cellulose blank 1 a is placed between the negative forming mould part 2 b and the massive flexible membrane 4. The positive forming mould part 2 a is pushing the massive flexible membrane 4 and the cellulose blank 1 a into the negative forming mould part 2 b when the forming pressure, F, is applied to the forming mould parts, as shown in FIGS. 8a-b . When forming the cellulose product, the negative forming mould part 2 b is heated to a forming mould part temperature T₂ and during the forming process, the cellulose blank 1 a is heated to a forming temperature T₁, see FIGS. 8a -c.

In FIGS. 9a-c another alternative forming mould 3 with a negative forming mould part 2 b and a positive forming mould part 2 a is schematically shown. The negative forming mould part 2 b is applying a forming pressure, F, on a massive flexible membrane 4, which is applying an isostatic pressure on the cellulose blank 1 a when forming the cellulose product. The massive flexible membrane 4 is constructed so that when the pressure, F, is applied from the forming mould parts, the massive flexible membrane 4 deforms in order to provide the isostatic pressure. The massive flexible membrane 4 may be of the same construction as described above in relation to the embodiment shown in FIGS. 8a-c . In the embodiment shown in FIGS. 9a-c , the massive flexible membrane 4 has a varied thickness to match the shape of the positive forming mould part 2 a. Due to the flexible properties of the massive flexible membrane 4, the massive flexible membrane 4 applies an isostatic pressure to the cellulose blank 1 a.

In FIG. 9a , the cellulose blank 1 a is placed between the positive forming mould part 2 a and the massive flexible membrane 4. The positive forming mould part 2 a is pushing the cellulose blank 1 a into the negative forming mould part 2 b towards the massive flexible membrane 4 when the forming pressure, F, is applied to the forming mould parts, as shown in FIGS. 9a-b . When forming the cellulose product, the positive forming mould part 2 a is heated to a forming mould part temperature T₂ and during the forming process, the cellulose blank 1 a is heated to a forming temperature T₁, see FIGS. 9a -c.

In the claims, the word “comprising” does not exclude other elements or steps, and the indefinite article “a” or “an” does not exclude a plurality. The mere fact that certain measures are recited in mutually different dependent claims does not indicate that a combination of these measured cannot be used to advantage

It will be appreciated that the above description is merely exemplary in nature and is not intended to limit the present disclosure, its application or uses. While specific examples have been described in the specification and illustrated in the drawings, it will be understood by those of ordinary skill in the art that various changes may be made and equivalents may be substituted for elements thereof without departing from the scope of the present disclosure as defined in the claims. Furthermore, modifications may be made to adapt a particular situation or material to the teachings of the present disclosure without departing from the essential scope thereof.

Therefore, it is intended that the present disclosure not be limited to the particular examples illustrated by the drawings and described in the specification as the best mode presently contemplated for carrying out the teachings of the present disclosure, but that the scope of the present disclosure will include any embodiments falling within the foregoing description and the appended claims.

Reference signs mentioned in the claims should not be seen as limiting the extent of the matter protected by the claims, and their sole function is to make claims easier to understand. 

1. A method for manufacturing a cellulose product having a non-flat product shape by a pressure moulding apparatus comprising a forming mould, the forming mould having at least two openable and closable negative forming surfaces or parts defining said product shape, comprising the steps of: arranging a cellulose blank with loose and separated fibres containing less than 45 weight percent water in said forming mould; heating said cellulose blank to a forming temperature in the range of 100° C. to 200° C.; and pressing said cellulose blank by means of said forming mould with a forming pressure acting on the cellulose blank across said forming surface, said forming pressure being in the range of 1 MPa to 100 MPa, wherein an isostatic pressure is obtained in force defined compressing devices, wherein said compressing devices comprises a flexible barrier or a membrane separating the cellulose blank from a pressure media, wherein: said forming mould comprises the flexible barrier or membrane and said pressure moulding apparatus further comprises a fluid control device for controlling a fluid, the pressure media, to exert the isostatic pressure on said cellulose blank via said fluid impermeable membrane.
 2. The method according to claim 1, wherein said cellulose blank contains less than 25 weight percent water, specifically less than 15 weight percent water.
 3. The method according to claim 1, wherein said cellulose blank comprises wood pulp, specifically at least 90 weight percent wood pulp.
 4. The method according to claim 1, wherein said step of heating at least partly takes place before said step of pressing.
 5. The method according claim 1, wherein the forming mould comprises a forming mould part and pressure mould part and at least one of said forming mould part and pressure mould part is heated before said step of pressing.
 6. A pressure moulding apparatus for manufacturing a cellulose product having a non-flat product shape starting from a cellulose blank with loose and separated fibres comprising: a forming mould at least two openable and closable negative forming surfaces or parts defining said product shape, wherein an isostatic pressure is obtained in force defined compressing devices, wherein said compressing devices comprises a flexible barrier or a membrane surrounding and separating the cellulose blank from a pressure media, wherein: said forming mould comprises the flexible barrier or membrane; and said pressure moulding apparatus further comprises a fluid control device configured to control a fluid, the pressure media, to exert the isostatic pressure on said cellulose blank via said fluid impermeable membrane, wherein, the flexible membrane is arranged between said fluid control device and said cellulose blank.
 7. A cellulose product having a non-flat shape comprising compressed loose and separated fibres, wherein the cellulose product is a hollow bottle.
 8. A cellulose product according to claim 7, wherein the cellulose product is mainly uniform in thickness. 